Introduction
Babbitt alloys remain consistent from edge-to-edge and end-to-end through thousands of pounds of ingots and bars, and through thousands of miles of spray wire. Babbitt formulations meet or exceed their engineering standards. With higher productivity, less rework, less cleanup. Fewer defects and higher quality finished products.
The coatings are ductile, low in oxides and exhibit a bright,metallic appearance.
It can Equivalent to: Tafa 04T, Sulzer Metco Spraybabbit
Surface Preparation
Surface should be clean, white metal, with no oxides (rust), dirt, grease, or oil on the surface to be coated. Note: It is best not to handle surfaces after cleaning. Recommended method of preparation is, to grit blast with 24 mesh aluminum oxide, rough grind, or rough machine in a lathe.
Application
Bearing Surfaces
Product Details
Chemical composition:
Type |
Chemical composition |
Sn |
Sb |
Cu |
other |
Babbitt wire |
90 |
7~8 |
3~4 |
0.25 |
Specifications
Grade |
AWS |
Babbitt wire |
C2.25 / C2.25M W-SnSbCu-1 |
Physical Properties
Grade |
Density |
Melting point |
Babbitt wire |
6.67 g/cm3 |
354 °C |
Typical Deposit Characteristics:
Typical Hardness |
Bond Strength |
Deposit Rate |
Deposit Efficiency |
Machilityineab |
Nil |
3000 psi |
48 lbs /hr/100A |
70% |
Good |
Standard Sizes & Packing:
Diameter |
Packing |
Wire Weight |
1/8(3.17mm) |
D 300 Spool |
15kg(33 lbs)/spool |