Wisdom Brand for Flame Spray Fecrbsi Wire

Product Description

FeCrBSi wire material with iron weight content as high as 80%. The coating was prepared by twin-wire arc spraying processing. The chemical compositions of the coating, 
as well as phase components were analyzed by energy-dispersive spectroscopy and 
x-ray diffraction method. The surface roughness, porosity, and cross-sectional morphology were further characterized. In-boiler test was also carried out. 
The low thickness loss of the tube indicates a promising application future in sludge boilers. 
The coating hardness is close to that of the commercial Armacor M and Armacor C materials.
 
It can Equivalent to TAFA 95MAX, Armacore M.
 
Surface Preparation 
Surface should be clean, white metal, with no oxides (rust), dirt, grease, or oil on the surface to be coated. Note: It is best not to handle surfaces after cleaning. Recommended method of preparation is, to grit blast with 24 mesh aluminum oxide, rough grind, or rough machine in a lathe.
 
Typical Applications
Boiler Tubes & Tube Shields,Yankee Dryer Rolls 
Anti-Skid ,Fan Blades 
Drill Collars.
Chemical Composition:
 

Grade	Chemical Composition
	Cr%	B%	Mn%	Si%	Fe%
FeCrBSi	29	3-4	1.5-2	1-2	Bal

 
 
Physical Properties:

Grade	Density	Melting point °C
FeCrBSi	7.3g/cm3	1538

 Typical Deposit Characteristics:

Typical Hardness	Bond Strength	Deposit Rate	Deposit Efficiency	Machilityineab
HRC 55-60	6000 psi	10 lbs/hr/100A	70%	Good

 
 
Standard Sizes & Packing:

Diameter	Packing	Wire Weight
1/16 Inch (1.6mm)	D 300 Spool	15kg(33lb)/spool

Other sizes (diameter and wire weight) can produced based on customers' need.