Wisdom Brand FeCrBSi Core wire Used for Thermal Spray Coating
Introduction
FeCrBSi wire material with iron weight content as high as 80%. The coating was prepared by twin-wire arc spraying processing. The chemical compositions of the coating, as well as phase components were analyzed by energy-dispersive spectroscopy and x-ray diffraction method. The surface roughness, porosity, and cross-sectional morphology were further characterized. In-boiler test was also carried out. The low thickness loss of the tube indicates a promising application future in sludge boilers. The coating hardness is close to that of the commercial Armacor M and Armacor C materials.
It can Equivalent to TAFA 95MAX, Armacore M.
Surface Preparation
Surface should be clean, white metal, with no oxides (rust), dirt, grease, or oil on the surface to be coated. Note: It is best not to handle surfaces after cleaning. Recommended method of preparation is, to grit blast with 24 mesh aluminum oxide, rough grind, or rough machine in a lathe.
Typical Applications
l Boiler Tubes & Tube Shields,Yankee Dryer Rolls
l Anti-Skid ,Fan Blades
l Drill Collars.
Chemical Composition:
| Grade | Chemical Composition |
| Cr% | B% | Mn% | Si% | Fe% |
| FeCrBSi | 29 | 3-4 | 1.5-2 | 1-2 | Bal |
Physical Properties:
| Grade | Density | Melting point °C |
| FeCrBSi | 7.3g/cm3 | 1538 |
Typical Deposit Characteristics:
| Typical Hardness | Bond Strength | Deposit Rate | Deposit Efficiency | Machilityineab |
| HRC 55-60 | 6000 psi | 10 lbs/hr/100A | 70% | Good |
Standard Sizes & Packing:
| Diameter | Packing | Wire Weight |
| 1/16 Inch (1.6mm) | D 300 Spool | 15kg(33lb)/spool |
Other sizes (diameter and wire weight) can produced based on customers' need.