1.6mm FeCrBSi powder cored wire For Arc Spray
Introduction
FeCrBSi wire material with iron weight content as high as 80%. The coating was prepared by twin-wire arc spraying processing. The chemical compositions of the coating, as well as phase components were analyzed by energy-dispersive spectroscopy and x-ray diffraction method. The surface roughness, porosity, and cross-sectional morphology were further characterized. In-boiler test was also carried out. The low thickness loss of the tube indicates a promising application future in sludge boilers. The coating hardness is close to that of the commercial Armacor M and Armacor C materials.
It can Equivalent to TAFA 95MAX, Armacore M.
Surface Preparation
Surface should be clean, white metal, with no oxides (rust), dirt, grease, or oil on the surface to be coated. Note: It is best not to handle surfaces after cleaning. Recommended method of preparation is, to grit blast with 24 mesh aluminum oxide, rough grind, or rough machine in a lathe.
Typical Applications
l Boiler Tubes & Tube Shields,Yankee Dryer Rolls
l Anti-Skid ,Fan Blades
l Drill Collars.
Chemical Composition:
| Grade |
Chemical Composition |
| Cr% |
B% |
Mn% |
Si% |
Fe% |
| FeCrBSi |
29 |
3-4 |
1.5-2 |
1-2 |
Bal |
Physical Properties:
| Grade |
Density |
Melting point °C |
| FeCrBSi |
7.3g/cm3 |
1538 |
Typical Deposit Characteristics:
| Typical Hardness |
Bond Strength |
Deposit Rate |
Deposit Efficiency |
Machilityineab |
| HRC 55-60 |
6000 psi |
10 lbs/hr/100A |
70% |
Good |
Standard Sizes & Packing:
| Diameter |
Packing |
Wire Weight |
| 1/16 Inch (1.6mm) |
D 300 Spool |
15kg(33lb)/spool |
Other sizes (diameter and wire weight) can produced based on customers' need.