Euqal to for Tafa06T Wire build-up coating and sealing
Introduction
Monel400
Monel 400 shows high strength and excellent corrosion resistance in a range of acidic and alkaline environments and especially suitable for reducing conditions. It also has good ductility and thermal conductivity.
It can Equivalent to: Tafa70T.
Surface Preparation
Surface should be clean, white metal, with no oxides (rust), dirt, grease, or oil on the surface to be coated. Note: It is best not to handle surfaces after cleaning. Recommended method of preparation is, to grit blast with 24 mesh aluminum oxide, rough grind, or rough machine in a lathe.
Application
Ceramic Under Coat
Oxidation Resistance
High Temperature
Chemical Composition
| Type | Composition |
| Ni | Fe | Cu | C | Mn | Si | S |
| Monel 400 | Min 63 | Max 2.5 | 28-34 | Max 0.3 | Max 2 | Max 0.5 | Max 0.024 |
Physical Properties
| Grade | Density | Melting Point |
| Monel 400 | 8.83g/cm3 | 1350 |
Typical Deposit Characteristics
| Typical Hardness | Bond Strength | Deposit Rate | Deposit Efficiency | Machilityineab |
| HRB 84 | 4310 psi | 10 lbs /hr/100A | 70% | Good |
Standard Sizes & Packing
| Diameter | Packing | Wire Weight |
| 1/16 (1.6mm) | D 300 Spool | 15kg/spool |
Other sizes (diameter and wire weight) can be produced by customers' requirement.